Building Mortar Tensile Bond Strength Tensile Testing Machine

1.introductions

Building mortar bonding strength tensile testing machine is to measure and determine bonding strength of building mortar made of inorganic cementitious materials, fine aggregates and admixtures as main materials and the building mortar is used for masonry, plastering ground engineering and other purposes of industrial and civil buildings.

2. test method for building mortar bonding strength tensile test

JGJ/T 70 standard for test method of performance on building mortar

3. Relative manufacturing and calibrating test method for Building Mortar Tensile Bond Strength Tensile Testing Machine

GB/T2611 general requirements for testing machines

GB/T16491 electronic universal testing machine

GB/T16825.1 verification of static uniaxial testing machines --- part 1: tension / compression testing machines --- verification and calibration of the force measuring system

ISO7500-1 metallic materials--- verification of static uniaxial testing machine --- part 1: tension / compression testing machines --- verification and calibration of the force measuring system

ASTM E4 standard practice for force verification of testing machines

EN 10002-2 tensile testing of metallic materials --- part 2: verification of the force measuring system of the tensile testing machine

4. specifications

building mortar tensile bond strength, tensile bond strength testing, mortar testing machine, tensile testing of building materials, bond strength test machine, mortar adhesion strength, tensile testing machine for mortar, ASTM C1583, ISO 13007, cement mortar tensile test, mortar adhesion testing, construction materials testing, bond strength test standards, tensile test for adhesives, compressive and tensile testing of mortar, concrete bond strength tester, building material tensile testing machine, adhesion properties of mortar, mortar specimen preparation, mortar pull of testing, tensile adhesion strength, mortar pull off test, bonding strength testing machine, adhesion resistance of mortar, ASTM C1583 bond strength test, mortar test equipment, bond strength of mortar to substrates, ISO 4624 adhesion test, mortar tensile strength test, tensile bond strength test procedure, mortar bonding agents, mortar bonding test machine, surface preparation for tensile testing, tensile force measurement, cement based adhesive testing, drying time and tensile strength, mortar interface strength testing, substrate influence on mortar adhesion, concrete surface bond strength, surface roughness effect on bond strength, building material tensile test standards, bonding strength of cement mortar, adhesive bonding testing, tensile bonding strength of construction materials, mortar substrate interaction, pull off adhesion tester, tensile testing of cementitiouis materials, bond failure mechanism, bonding capacity of mortar, shear and tensile bond strength, roughness of substrate abd bond strength, bond strength of gout to concrete, cement mortar bondign evaluation, surface treatment and bond strength, testing mortar adhesion to ceramic tiles, mortar pull off adhesion test procedure, concrete bonding strength tester, tensile strength and material compatibility, mortar bond durability testing, cementitious material bond failure, ISO 11056 testing standard for mortar, building material adhesion strength tester

How to Select the Right Tensile, Compression, Bending, Shear, Peel, and Tear Testing Machine: Calculation Formulas with Examples

Selecting the appropriate testing machine for tensile, compression, bending, shear, peel, and tear tests requires careful consideration of multiple factors, including the force range, specimen dimensions, test standards, and machine capabilities. Below are the key calculation formulas to help determine the necessary machine specifications, along with examples for better understanding.

1. Tensile Testing Machine Selection

Tensile testing machines measure the maximum tensile strength and elongation of materials.

Key Formula:

F_max=σ_max × A

Where:

F_max = Maximum required force (N)

σ_max = Ultimate tensile strength of the material (MPa)

A = Cross-sectional area of the specimen (mm²)

Example: For a steel specimen with σ_max =400MPa and cross-sectional area A =100mm²:

F_max=400 × 100=40,000N (40kN)

A 50 kN tensile testing machine would be suitable.

2. Compression Testing Machine Selection

Compression tests determine a material's resistance to compressive forces.

Key Formula:

F_max=σ_c × A

Where:

F_max = Maximum required force (N)

σ_c = Compressive strength of the material (MPa)

A = Cross-sectional area of the specimen (mm²)

Example: For a concrete cube with σ_c =30MPa and A =150²=22,500mm²:

F_max=30 × 22,500=675,000N (675kN)

A 1000 kN compression testing machine would be ideal.

3. Bending Testing Machine Selection

Bending tests evaluate the flexural strength of materials.

Key Formula for Three-Point Bending:

Where:

σ_f = Flexural stress (MPa)

F= Applied force (N)

L= Span length (mm)

b= Width of the specimen (mm)

h= Thickness of the specimen (mm)

Example: For a wooden beam with L=500mm, b=50mm, h=25mm, and requiring a stress of 10 MPa:

A 5 kN bending tester would be suitable.

4. Shear Testing Machine Selection

Shear tests determine the shear strength of materials.

Key Formula:

F_max=τ × A

Where:

F_max = Maximum shear force (N)

τ= Shear strength of the material (MPa)

A = Shear area (mm²)

Example: For an aluminum sheet with τ=90 MPa and A=200mm²:

F_max=90×200=18,000N(18kN)

A 20 kN shear testing machine is recommended.

5. Peel Testing Machine Selection

Peel tests measure the adhesion strength between bonded materials.

Key Formula:

Where:

P= Peel strength (N/mm)

F= Measured force (N)

W= Width of the specimen (mm)

Example: For a tape with F=50N and W=25mm:

A peel testing machine with at least 5 N force capacity is required.

6. Tear Testing Machine Selection

Tear tests determine the resistance of a material to tearing forces.

Key Formula:

Where:

F_tear= Tear strength (N/mm)

F= Measured force (N)

t= Thickness of the specimen (mm)

Example: For a rubber sheet with F=100N and t=2mm:

A tear testing machine with 100 N capacity is needed.

When selecting a testing machine, ensure that the maximum force capacity of the machine is at least 1.2 to 1.5 times the calculated force to account for safety margins and unexpected variations. Additionally, consider compliance with relevant test standards (ASTM, ISO, GB, EN, JIS) and machine features such as speed control, data acquisition, and test automation.

By using the above formulas and examples, engineers and manufacturers can accurately determine the appropriate testing machine specifications for their specific material and application requirements.